层状双氢氧化物和蒙脱石的剥离及其自组装

doi:10.13218/j.cnki.csdc.2018.07.006

摘要/Abstract

摘要： 以钙基蒙脱石为原料,氟化钠为钠化剂,十六烷基三甲基溴化铵为有机改性剂采用离子交换法制备了有机蒙脱石(CTA-MMT);以硝酸镁、硝酸铝、氢氧化钠和十二烷基磺酸钠为原料,采用水热法制备了有机型镁铝层状双氢氧化物(MgAl-SDS-LDH);以氯仿为剥离介质,采用超声法剥离CTA-MMT和MgAl-SDS-LDH,分别获得了两种剥离型矿物溶胶,将其混合自组装制备了蒙脱石/层状双氢氧化物(MMT/LDH)组装材料。用XRD和AFM表征了CTA-MMT和MgAl-SDS-LDH及其剥离产物,并分析了组装材料的热稳定性。结果表明,CTA-MMT和MgAl-SDS-LDH在氯仿介质中剥离仅需20 min,剥离型CTA-MMT和MgAl-SDS-LDH片层平均厚度分别约为9和8 nm。MMT/LDH由剥离型CTA-MMT和MgAl-SDS-LDH片层有序组装而成,组装材料结构与MgAl-SDS-LDH和CTA-MMT的含量有关,其结构单元层间距2.59 nm(CTA-MMT含量较低时)随着组装材料中CTA-MMT含量的升高而转变为1.82 nm。MMT/LDH组装材料具有较单一的CTA-MMT或MgAl-SDS-LDH更高的热稳定性。

关键词: 表面活性剂, 蒙脱石, 层状双氢氧化物, 氯仿, 剥离, 自组装

Abstract: Organic montmorillonite (CTA-MMT) was prepared with the method of ion exchange by using calcium-montmorillonite as raw material,sodium fluoride as sodium agent and cetyltrimethylammonium bromide (CTAB) as organic modifier.Organic layered double hydroxide (MgAl-SDS-LDH) was synthesized by hydrothermal method by using the raw materials of magnesium nitrate,aluminum nitrate,sodium hydroxide and sodium dodecyl sulfonate (SDS).Sols of exfoliated CTA-MMT and exfoliated MgAl-SDS-LDH were obtained by exfoliation of CTA-MMT and MgAl-SDS-LDH in chloroform through ultrasonication.By mixing the two sols,montmorillonite/layered double hydroxide nanocomposite (MMT/LDH) was prepared by self-assembly of exfoliated products.The structures of CTA-MMT,MgAl-SDS-LDH and their exfoliated products were characterized by XRD and AFM.The thermal stability of MMT/LDH was characterized by thermogravimetric analysis.The results show that CTA-MMT and MgAl-SDS-LDH can be exfoliated in chloroform in merely 20 min.The average thicknesses of exfoliated CTA-MMT and exfoliated MgAl-SDS-LDH are about 9 and 8 nm,respectively.MMT/LDH is a self-assembling material which is assembled orderly by exfoliated CTA-MMT and exfoliated MgAl-SDS-LDH,and the structure of MMT/LDH is influenced by the content of exfoliated MgAl-SDS-LDH and exfoliated CTA-MMT.The interlayer spacing of MMT/LDH decreases with the increase of content of exfoliated CTA-MMT,from 2.59 nm (in the case of low content of CTA-MMT) to 1.82 nm (in the case of high content of CTA-MMT).Furthermore,the thermostability of MMT/LDH is better than that of pristine CTA-MMT or MgAl-SDS-LDH.

Key words: surfactant, montmorillonite, layered double hydroxide, chloroform, exfoliation, self-assembly

中图分类号:

TQ423.9

戴璐逊,梁少彬,陈耀,谢襄漓,李存军,王林江. 层状双氢氧化物和蒙脱石的剥离及其自组装[J]. 日用化学工业, 2018, 48(7): 392-398.

DAI Lu-xun,LIANG Shao-bin,CHEN Yao,XIE Xiang-li,LI Cun-jun,WANG Lin-jiang. Exfoliation of layered double hydroxide and montmorillonite and their self-assembly[J]. China Surfactant Detergent & Cosmetics, 2018, 48(7): 392-398.

参考文献

[1] Nicolosi V,Chhowalla M,Kanatzidis M G,et al.Liquid exfoliation of layered materials [J].Science,2013,340(6139):1226419.
[2] Li C J.Preparation of LDH/MMT nanocomposite based on the exfoliation and assembly behavior of monotmorillonite [D].Guilin:Guilin University of Technology,2015.
[3] Sun H J,Peng T J,Lin Y.Calculation of crystal chemical formula of montmorillonite and classification [J].Journal of Synthetic Crystals,2008,37(2):350-355.
[4] Mao L L,Wang H Z,Wang Q.Preparation of layered magnesium hydroxide aluminum and its adsorption of free fatty acids (FFAs) from biodiesel [J].Journal of Synthetic Crystals,2014,43(6):1520-1524.

[5] Qiu J,Lv X J.Organic modification technics and gel performance of montmorillonite [J].Industrial Minerals and Processing,2008(1):7-10.
[6] Li C J,Lu H,Lin Y Y,et al.Self-sacrificial templating synthesis of self-assembly 3D layered double hydroxide nanosheets using nano-SiO₂ under facile conditions [J].RSC Advances,2016,6(99):97237-97240.
[7] Hibino T,Jones W.New approach to the delamination of layered double hydroxides [J].2001,11(5):1321-1323.
[8] Antonyraj C A,Churchil A,Koilraj P,et al.Synthesis of delaminated LDH:a facile two step approach [J].Chemical Communications,2010,46(11):1902-1904.
[9] Venugopal B R,Shivakumara C,Rajamathi M.Effect of various factors influencing the delamination behavior of surfactant intercalated layered double hydroxides [J].Journal of Colloid and Interface Science,2006,294(1):234-239.
[10] He X J,Wang L J,Xie X L,et al.Investigation of thermal property and flame retardancy of ABS/montmorillonite nanocomposites [J].Plastics,Rubber and Composites,2010,39(2):54-60.
[11] Liang Q C,Chen Yao,Li C J,et al.Intercalation assembly of acetate intercalated layered double hydroxide and montmorillonite [J].Journal of Synthetic Crystals,2015,44(10):2874-2880.
[12] Zhu J X,He H P,Juo J G,et al.Comparative study of the aggregation of different long-chain alkylammonia in montmorillonite [J].Acta Mineralogica Sinica,2003,23(3):194-197.
[13] Chen Y,Xie X L,Li C J,et al.Preparation of heterogeneous films by layer-by-layer self-assembly based on exfoliation of montmorillonite and layered double hydroxide [J].Journal of Synthetic Crystals,2016,45(5):1293-1298.
[14] Liu Z P,Ma R Z,Osada M,et al.Synthesis,anion exchange,and delamination of Co-Al layered double hydroxide:assembly of the exfoliated nanosheet/polyanion composite films and magneto-optical studies [J].Journal of the American Chemical Society,2006,128(14):4872-4880.
[15] Yi D,Yang R,Wilkie C A.Layered double hydroxide-montmorillonite-a new nano-dimensional material [J].Advances in Polymer Technology,2013,24(2):204-209.