SBA-15复合材料的制备及其催化合成环己酮乙二醇缩酮

doi:10.13218/j.cnki.csdc.2017.11.009

日用化学工业 ›› 2017, Vol. 47 ›› Issue (11): 641-644.doi: 10.13218/j.cnki.csdc.2017.11.009

SBA-15复合材料的制备及其催化合成环己酮乙二醇缩酮

向诗银, 李志鹏, 杨水金

湖北师范大学化学化工学院,湖北黄石 435002

收稿日期:2017-07-06 出版日期:2017-11-22 发布日期:2019-03-21
通讯作者: 杨水金,教授,电话:(0714)6515602,E-mail:yangshuijin@hbnu.edu.cn。
作者简介:向诗银(1993-),男,湖北广水人,硕士研究生,电话:18271625022,E-mail:1483293539@qq.com。
基金资助:
湖北省自然科学基金重点资助项目(2014CFA131)

Preparation of SBA-15 and its catalytic performance in
synthesis of cyclohexanone ethylene ketal

XIANG Shi-yin, LI Zhi-peng, YANG Shui-jin

College of Chemistry and Chemical Engineering,Hubei Normal University,Huangshi,Hubei 435002,China

Received:2017-07-06 Online:2017-11-22 Published:2019-03-21

摘要/Abstract

摘要： 将金属离子嫁接在SBA-15的孔道中作为催化剂,考察其催化合成环己酮乙二醇缩酮的性能。使用FT-IR、SEM和XRD对催化剂的结构进行表征,结果表明合成的催化剂为目标催化剂。固定环己酮用量为0.2 mol,当乙二醇与环己酮的摩尔比为1.7∶1,催化剂的用量为反应底物质量的1.2%,带水剂环己烷的用量为14 mL,反应时间为100 min时,Co/SBA-15催化合成效果最好,环己酮乙二醇缩酮的收率为89.8%。

关键词: 香料, 环己酮乙二醇缩酮, 介孔材料, 合成

Abstract: Metal ions were grafted into the pores of SBA-15 and the grafted product was examined for using as catalyst in synthesis of cyclohexanone ethylene ketal.Structure of the catalyst was characterized by FT-IR,SEM and XRD.And the characterizing results show that the catalyst prepared is the targeted one.Then,experiment for the synthesis of cyclohexanone ethylene ketal was carried out with various catalysts.Experimental results show that as dosage of cyclohexanone is fixed at 0.2 mol;molar ratio of glycol to cyclohexanone is 1.7∶1;dosage of the catalyst is 1.2% (mass) of the reactants;volume of water stripping agent,cyclohexane is 14 mL;reaction time is 100 min;catalyst Co/SBA-15 displays the best result that the yield of cyclohexanone ethylene ketal achieves 89.8%.

Key words: perfumes, cyclohexanone ethylene ketal, mesoporous materials, synthesis

中图分类号:

TQ655

向诗银, 李志鹏, 杨水金. SBA-15复合材料的制备及其催化合成环己酮乙二醇缩酮[J]. 日用化学工业, 2017, 47(11): 641-644.

XIANG Shi-yin, LI Zhi-peng, YANG Shui-jin. Preparation of SBA-15 and its catalytic performance in
synthesis of cyclohexanone ethylene ketal[J]. China Surfactant Detergent & Cosmetics, 2017, 47(11): 641-644.

参考文献

[1] 向诗银,杨水金.H₆P₂Mo₉W₉O₆₂/Cu₃(BTC)₂的制备及催化合成缩醛(酮)[J].日用化学工业,2017,47(5):281-285.
[2] 许招会,廖维林,王甡.磷钨酸镧催化合成缩醛(酮)的研究[J].分子催化,2008,22(1):39-43.
[3] 徐明波,刘晓,王娟,等.二氧化硅负载磷钨酸催化合成环己酮1,2-丙二醇缩酮[J].日用化学工业,2012,42(6):440-442,451.
[4] 魏云霞,马明广,李生英,等.磷钨杂多酸银盐催化合成缩酮(醛)[J].无机化学学报,2012,28(9):1903-1909.
[5] 何节玉,廖德仲,毛立新,等.镧掺杂硫酸钛的酸性及催化缩酮活性[J].分子催化,2005,19(2):109-114.
[6] 杨水金,王强,段国滨,等.H₄SiW₁₂O₄₀/ZrO₂-Al₂O₃催化合成丁酮1,2-丙二醇缩酮[J].徐州工程学院学报,2012,27(3):22-26.
[7] 张萌,杨亚提,秦睿,等.二胺基改性有序多孔SBA-15对溶液中Cd²⁺离子的吸附研究[J].环境科学,2013,34(7):2677-2685.
[8] 宋明娟,邹成龙,牛国兴,等.(NH₄)₂SiF₆预处理改善SBA-15介孔材料的水热稳定性[J].催化学报,2012,33(1):140-151.
[9] 李志雄,纳薇,王华,等.Cu-Zn-Zr/SBA-15介孔催化剂的制备及CO₂加氢合成甲醇的催化性能[J].高等学校化学学报,2014,35(12):2616-2623.
[10] 李荣华,岳庆玲,孟昭福,等.氨基改性SBA-15有序介孔材料对Cd(Ⅱ)的吸附热力学特征研究[J].环境科学学报,2011,31(6):1241-1247.
[11] 王青春,安胜利,彭军,等.杂原子富集的球状M/SBA-15(M=Al,Fe,Ni)介孔分子筛的控制合成及表征[J].材料导报B:研究篇,2016,30(4):56-60.
[12] Wang L,Yang R T.Increasing selective CO₂ adsorption on amine-grafted SBA-15 by increasing silanol density [J].Journal of Physical Chemistry C,2017,115(43):21264-21272.
[13] Xing S,Lv P,Fu J,et al.Direct synthesis and characterization of pore-broadened Al-SBA-15 [J].Microporous & Mesoporous Materials,2017,239:316-327.
[14] Carrero A,Vizcaíno A J,Calles J A,et al.Hydrogen production through glycerol steam reforming using Co catalysts supported on SBA-15 doped with Zr,Ce and La [J].Journal of Energy Chemistry,2017,26(1):42-48.
[15] Malik R,Rana P S,Tomer V K,et al.Nano gold supported on ordered mesoporous WO₃/SBA-15 hybrid nanocomposite for oxidative decolo-rization of azo dye [J].Microporous & Mesoporous Materials,2016,225:245-254.
[16] Meloni D,Perra D,Monaci R,et al.Transesterification of Jatrophacurcas oil and soybean oil on Al-SBA-15 catalysts [J].Applied Cata-lysis B Environmental,2016,184:163-173.
[17] 杨水金,徐玉林,龚文朋,等.H₄SiW₆Mo₆O₄₀/SiO₂促进一锅法合成4-苯基-6-甲基-5-乙氧羰基-3,4-二氢嘧啶-2(H)酮[J].徐州工程学院学报,2014,29(2):11-16.
[18] 吕宝兰,黎杉珊,杨水金.磷钨酸/硅胶催化剂催化合成环己酮乙二醇缩酮[J].精细石油化工进展,2011,12(12):50-52.
[19] 章爱华,尹笃林,刘文萍,等.活性炭负载对甲苯磺酸催化微波合成环己酮乙二醇缩酮[J].光谱实验室,2009,26(5):1186-1189.
[20] 刘徐,刘汉文,唐子龙,等.环己酮乙二醇缩酮的微波合成研究[J].精细化工中间体,2007,37(1):43-45.
[21] 杨水金,李晓萍.分子筛MCM-48负载硅钨酸催化合成环己酮乙二醇缩酮[J].稀有金属,2009,33(4):573-576.
[22] 杨赟,谢萍,黄永葵,等.二氧化硅负载磷钨钼酸催化合成环己酮乙二醇缩酮[J].精细石油化工进展,2011,12(8):54-57.

SBA-15复合材料的制备及其催化合成环己酮乙二醇缩酮

Preparation of SBA-15 and its catalytic performance in
synthesis of cyclohexanone ethylene ketal

PDF (PC)

赞

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

Metrics

本文评价

推荐阅读 10

[1]	艾浩康, 姜亚洁, 王亚魁, 张璐, 耿涛. 硬脂酸酯双子季铵盐的合成及性能研究[J]. 日用化学工业（中英文）, 2024, 54(1): 16-23.
[2]	崔丛丛,张红丽,玄光善. 多头季铵盐表面活性剂的合成及性能评价[J]. 日用化学工业（中英文）, 2023, 53(8): 899-907.
[3]	周媛, 杨秀全, 张军, 白亮, 吴志宇. 不同酯化度烷基糖苷磺基琥珀酸酯盐的合成与性能[J]. 日用化学工业（中英文）, 2023, 53(7): 765-772.
[4]	王玮, 邢玉瑾, 张雪. 气相色谱-质谱法测定化妆品中19种香精香料[J]. 日用化学工业（中英文）, 2023, 53(5): 581-587.
[5]	李晓敏. 基于酶催化合成单甘油酯工艺优化及抑菌活性研究[J]. 日用化学工业（中英文）, 2023, 53(2): 180-186.
[6]	肖璐, 荣群, 白希, 莫洪波, 范维刚. 环境污染物布洛芬吸附材料的研究进展[J]. 日用化学工业（中英文）, 2023, 53(12): 1437-1442.
[7]	王涛, 孙晓, 李卓, 董曼曼, 贾寒冰, 卫星华. 乙酰香兰素合成工艺优化及反应进程分析[J]. 日用化学工业（中英文）, 2023, 53(11): 1273-1279.
[8]	米浩宇,刘婉怡,段虹钰,张天春,韩鲁平. 玉米秸秆木聚糖的硫酸化修饰及抗氧化活性研究[J]. 日用化学工业, 2022, 52(9): 975-980.
[9]	赵淑芬,郑丹苗,刘华溪,宋松林,陈站,杨泞源,韦星船. 松香基双子表面活性剂合成及应用进展[J]. 日用化学工业, 2022, 52(8): 892-903.
[10]	张永涛,赵净沙,蒋雁冰,赵丹,王昌涛,李萌. 代谢工程改造酵母生产香料的研究进展[J]. 日用化学工业, 2022, 52(6): 645-655.
[11]	范婷,赵健烽,常烨珺,季乐. 重组人源化Ⅲ型胶原蛋白对皮肤功能性相关基因表达的影响[J]. 日用化学工业（中英文）, 2022, 52(12): 1326-1332.
[12]	范高宁. 类菌胞素氨基酸的性质及其在化妆品领域中应用的研究进展[J]. 日用化学工业（中英文）, 2022, 52(12): 1366-1372.
[13]	薛婉婷,李丽,董银卯,郭苗苗. 美白功效评价现状及发展趋势[J]. 日用化学工业, 2021, 51(9): 890-896.
[14]	任倩倩,吴华,金建明. 化妆品植物原料（IV）——抑制黑色素合成信号通路的植物美白原料的研究与开发[J]. 日用化学工业, 2021, 51(7): 590-597.
[15]	王军,张晨龙,杨许召,白亚榕. 磁性表面活性剂的研究进展[J]. 日用化学工业, 2021, 51(6): 546-553.

SBA-15复合材料的制备及其催化合成环己酮乙二醇缩酮

Preparation of SBA-15 and its catalytic performance in synthesis of cyclohexanone ethylene ketal

PDF (PC)

赞

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

Metrics

本文评价

推荐阅读 10

Preparation of SBA-15 and its catalytic performance in
synthesis of cyclohexanone ethylene ketal