丙三醇对壳聚糖溶液储存稳定性的影响

陈思佳(),易亚,张大伟()

东北林业大学生物质材料科学与技术教育部重点实验室,黑龙江哈尔滨 150040

收稿日期:2021-02-05 修回日期:2021-03-23 出版日期:2021-04-22 发布日期:2021-04-27
通讯作者: 张大伟
作者简介:陈思佳（1993-）,女,黑龙江青冈人,硕士,电话：18846773837,E-mail： ciga0623@163.com。
基金资助:
中央高校基本科研业务费专项资金项目(2572018BB10);中央高校基本科研业务费专项资金项目(2572017EB06)

Effects of glycerol on the storage stability of the chitosan solution

CHEN Si-jia(),YI Ya,ZHANG Da-wei()

Key Laboratory of Bio-based Material Science & Technology, Northeast Forestry University, Harbin, Heilongjiang 150040, China

Received:2021-02-05 Revised:2021-03-23 Online:2021-04-22 Published:2021-04-27
Contact: Da-wei ZHANG

摘要/Abstract

摘要：

研究了溶解在丙三醇（GL）/水混合溶剂中的壳聚糖（CS）黏度随储存时间、储存温度的变化规律,探讨了GL对CS溶液储存稳定性的影响。结果表明,室温时,GL的加入可以有效改善温度升高导致的CS溶液储存稳定性的下降趋势;相比于室温,1 ℃时,使用GL作为稳定剂的CS溶液体系在6.5 h内增比黏度几乎不变,放置99 h后,含有GL的CS溶液增比黏度也仅下降了3.8%,小于同等温度下水溶液中的CS增比黏度下降比例的1/2。GL的加入可以有效提高CS的储存稳定性,1 ℃下储存时,GL使CS溶液达到较佳的储存稳定性能。

关键词: 壳聚糖, 丙三醇, 黏度, 储存温度, 储存时间

Abstract:

The effects of glycerol （GL） on the storage stability of the chitosan （CS） solution were investigated by studying the variation of the viscosity of CS dissolved in GL/water mixed solvent with storage temperature and storage time. The results showed that, at room temperature, GL could effectively improve the decreasing trend of storage stability of CS solution caused by heating. Compared with room temperature, the specific viscosity of CS solution with GL as stabilizer was almost unchanged within 6.5 h at 1 ℃. After standing for 99 h, the specific viscosity of the CS solution containing GL was decreased by only 3.8%, less than half of the specific viscosity decrease in aqueous solution at the same temperature. The addition of GL could effectively improve the storage stability of CS. When the storage temperature was 1 ℃, the CS solution had better storage stability in the presence of GL.

Key words: chitosan, glycerol, viscosity, storage temperature, storage time

中图分类号:

TQ658

陈思佳,易亚,张大伟. 丙三醇对壳聚糖溶液储存稳定性的影响[J]. 日用化学工业, 2021, 51(4): 306-311.

CHEN Si-jia,YI Ya,ZHANG Da-wei. Effects of glycerol on the storage stability of the chitosan solution[J]. China Surfactant Detergent & Cosmetics, 2021, 51(4): 306-311.

图/表 6

图 1

图 2

图 3

图 4

图 5

表 1

参考文献 23

[1]	Liu Yongxu, Zhang Dawei. Preparation and properties of bacteriostatic chitosan/PVA/chitosan oligosaccharide nanofibrous membranes[J]. Biomass Chemical Engineering, 2020,54(4) : 30-36.
[2]	Patrulea V, Ostafe V, Borchard G, et al. Chitosan as a starting material for wound healing applications[J]. European Journal of Pharmaceutics and Biopharmaceutics, 2015,97:417-426. pmid: 26614560
[3]	Bao Wenyi, Xu Chen, Song Fei, et al. Effect of glycerol on mechanical properties of chitosan-starch composite edible film[J]. Acta Polymerica Sinica, 2015 ( 1) : 49-56.
[4]	Wen Huaqiang, Ma Jiahua, Wang Jing, et al. Preparation of hydrophobic chitosan and its hemostasis[J]. Fine Chemicals, 2018,35(8) : 1370-1375.
[5]	Lin Jinbin, Xu Hongda, Ye Wei, et al. Design and synjournal of Al³+-selective fluorescent probe based on chitosan derivative [J]. Chemical Reagents, 2019,41(2) : 182-185.
[6]	Yang Qi, Tang Lirong, Lin Fengcai, et al. Preparation and properties of nanocellulose/chitosan/gelatin composite films[J]. Biomass Chemical Engineering, 2018,52(1) : 17-22.
[7]	Mooibroek T J, Casas-Solvas J M, Harniman R L, et al. A threading receptor for polysaccharides[J]. Nature Chemistry, 2016,8(1) : 69-74. pmid: 26673266
[8]	Wang Ling, Zhou Jiao, Ma Xiaojun. Preparation of chitosan/poly(hydroxybutyrate-hydroxyhexanoate) biodegradable composite films[J]. Biomass Chemical Engineering, 2017,51(6) : 1-5.
[9]	Dong Lidan, Wei Changping, Li Zhongtian, et al. Preparation and properties of nano-chitosan composites[J]. Chinese Optics, 2018,11(5) : 773-778.
[10]	Zhang Wei, Tang Gang, Zhang Liying, et al. Application progress of nanomaterials in purification of heavy metal polluted water[J]. Chemical Industry and Engineering Progress, 2018,38(9) : 23-27.
[11]	Eladlani N, Dahmane E, Rhazi M, et al. Nanoparticles and whiskers-based chitosan films for Cr complexation[J]. Environmental Chemistry Letters, 2015,13(1) : 105-110.
[12]	Yang Huandie, Zhang Xiang, Alexander S, et al. Research progress of chitosan and chitooligosaccharide in bacteriostasis and preservation[J]. Shandong Agricultural Sciences, 2020,52(2) : 167-172.
[13]	Younes I, Sellimi S, Rinaudo M, et al. Influence of acetylation degree and molecular weight of homogeneous chitosans on antibacterial and antifungal activities[J]. International Journal of Food Microbiology, 2014,185:57-63. doi: 10.1016/j.ijfoodmicro.2014.04.029 pmid: 24929684
[14]	Yang Junjie, Hu Guangmin, Xiang Hengxue, et al. Progress in the research of chitosan dissolution behavior and its fibers[J]. Materials China, 2014,33(11) : 641-648,689.
[15]	Chen Xuanmo, Ning Wane, Peng Zeye, et al. Comparative study on solution properties of chitosan dissolved by formic acid and acetic acid[J]. Food Research and Development, 2020,41(15) : 23-29.
[16]	Zhang Keke. Preparation of chitosan shape memory polymer and characterization of solution actuation[D]. Harbin: Northeast Forestry University, 2017.
[17]	Ma Y, Xin L, Tan H, et al. Chitosan membrane dressings toughened by glycerol to load antibacterial drugs for wound healing[J]. Materials Science & Engineering C Materials for Biological Applications, 2017,81:522. doi: 10.1016/j.msec.2017.08.052 pmid: 28888006
[18]	Yang Shuai, Zhang Keke, Cui Jing, et al. Effect of temperature and concentration on the viscosity of chitosan solution in water/ethanol mixed[J]. Materials Reports, 2017,31(24) : 109-113.
[19]	Joel J T, Bulanadi J C, Wagner M, et al. Towards a less biased dissolution of chitosan[J]. Analytica Chimica Acta, 2016,935:258-268. doi: 10.1016/j.aca.2016.06.021 pmid: 27543035
[20]	Li Kexing, Jiang Xingke, Xia Wenshui. Study on rheological properties and application of chitosan solution[J]. Science and Technology of Food Industry, 2011,312(2) : 65-68,72.
[21]	Yang Junjie, Hu Guangmin, Xiang Hengxue, et al. Progress in the research of chitosan dissolution behavior and its fibers[J]. Materials China, 2014,33(11) : 641-648,689.
[22]	Huo Hongguang, Fang Bo, Jiang Tiqian. Experimental study on preparation and properties of immobilized L-asparaginase on chitosan modified[J]. Journal of East China University of Science and Technology, 2005,31(1) : 13-17.
[23]	Zhao Yucong, Jin Liuping, Chen Manru, et al. Effect of glycerol on mechanical properties of chitosan-starch composite edible film[J]. Packaging Engineering, 2019,40(21) : 68-73.

溶剂	体积变化率/%
100%水	6.38
80%水+20% GL	3.66

丙三醇对壳聚糖溶液储存稳定性的影响

Effects of glycerol on the storage stability of the chitosan solution

RichHTML

PDF (PC)

赞

可视化

摘要/Abstract

引用本文

使用本文

图/表 6

参考文献 23

相关文章 15

Metrics

本文评价

推荐阅读 10

[1]	郭芳. 乳化剂及增稠剂对低黏液晶乳液的影响[J]. 日用化学工业（中英文）, 2023, 53(1): 16-23.
[2]	张婉萍,吴凯翔,蒋汶,张冬梅. PR-CS/γ-PGA纳米胶囊的制备和表征[J]. 日用化学工业, 2022, 52(7): 710-716.
[3]	黄旭娟,王婷,丁正青,杨欣欣,蔡照胜,商士斌. 脱氢枞氧基聚氧乙烯缩水甘油醚接枝羟乙基壳聚糖制备及其表面活性[J]. 日用化学工业, 2022, 52(6): 594-600.
[4]	张云,李琛,于思涵,刘冬. 高悬浮能力清洁剂的制备与性能研究[J]. 日用化学工业, 2022, 52(3): 253-257.
[5]	隋振全,毛金超,徐桂云,范金石. 天然生物质材料的制备、性质与应用（Ⅰ）——自然界唯一的碱性多糖：甲壳素/壳聚糖[J]. 日用化学工业, 2022, 52(1): 7-14.
[6]	孟新宇,柳欢,胡学一,夏咏梅. 疏水改性壳聚糖的合成与乳化性能研究[J]. 日用化学工业, 2021, 51(8): 705-710.
[7]	李劲峰,高鹰,宁科功,张秋霞,刘萍,伍鹏,李黎仙. 一种低黏度悬浮液体系的开发研究[J]. 日用化学工业, 2021, 51(2): 132-138.
[8]	杜晶晶,韩肖惠,王博,徐靖,张彰. 壳聚糖改性高分子表面活性剂研究进展[J]. 日用化学工业, 2021, 51(1): 56-62.
[9]	张冉冉,杜玉兰,范培浩,张云贤. 油包水乳化体系稳定性的研究与分析[J]. 日用化学工业, 2020, 50(8): 566-571.
[10]	王优,左士祥,李霞章,刘文杰,徐荣,钟璟,姚超. 超细TiO₂在硅油中的流变特性与紫外保护性能[J]. 日用化学工业, 2020, 50(2): 112-117.
[11]	贾振勇,李萍,杨效益,郭朝华,李建波. 烷基化壳聚糖硫酸盐的制备及性能研究[J]. 日用化学工业, 2020, 50(11): 749-755.
[12]	肯生叶,李峰,饶国华,段勤,杨雪燕,邹由. 气相色谱法测定烟用香精中的乙醇、1,2-丙二醇和丙三醇[J]. 日用化学工业, 2019, 49(5): 346-350.
[13]	许格,郑延成,元平南,郑恒. 马来酸酯磺酸盐型活性聚合物的合成及性能研究[J]. 日用化学工业, 2019, 49(2): 76-82.
[14]	陈凯丽,刘冬,张云,倪鑫炯,曹玉华,曹光群. 氯化钠对包覆维生素C多重乳液的影响[J]. 日用化学工业, 2019, 49(12): 805-810.
[15]	任冬寅, 尚志新, 王启宝. 壳聚糖的接枝改性及其CO₂/N₂响应乳化性能研究[J]. 日用化学工业, 2018, 48(5): 260-265.