开放孔隙介孔氧化硅的合成及其在化妆品中的应用研究

doi:10.3969/j.issn.2097-2806.2025.11.008

Abstract

Abstract:

An open-pored mesoporous silica （OSMS） was successfully prepared by emulsion method. Its microstructure was analyzed using scanning electron microscopy （SEM）, transmission electron microscopy （TEM）, and nitrogen adsorption-desorption tests （BET）. The results showed that, the OSMS particles were monodisperse, and the particle size was 0.40 μm; the product had open channel structure and uniform mesopore size distribution （pore diameter of 24.4 nm）; OSMS had high specific surface area （162 m²/g） and large pore volume （1.12 cm³/g）. The results of performance study indicated that, in the oil absorption value test for 10 different oils and fats, OSMS demonstrated superior adsorption performance. Its oil absorption values were 1.3-1.9 times that of porous silica 150H, 3.3-6.3 times that of silicone elastomer KSP-100, and 6.0-7.5 times that of the starch-based TAPIOCA, respectively. Human skin oil-control experiments indicated that OSMS had the features of rapid and long-lasting adsorption, and the oil-control effect was linearly and positively correlated with the dosage （R²>0.95）. In vitro SPF value tests showed that OSMS had sun-screening synergistic effect, and just 0.3% （w/%） OSMS could increase the SPF value of a sunscreen. This work might provide experimental support for the application of OSMS as an oil-control raw material and a sun-screening synergist in cosmetics.

Key words: emulsion method, open pore structure, mesoporous silica, adsorption performance, synergistic sun-protection effect

CLC Number:

TQ658

Zhihui Zheng, Minjia Yuan, Wenxing Wang. Synthesis of open-pored mesoporous silica and its application in cosmetics[J].China Surfactant Detergent & Cosmetics, 2025, 55(11): 1428-1434.

Figures/Tables 7

Fig. 1

Fig. 2

Fig. 3

Tab. 1

Tab. 2

Fig. 4

Fig. 5

References 20

[1]	Kresge C T, Leonowicz M E, Roth W J, et al. Ordered mesoporous molecular sieves synthesized by a liquid-crystal template mechanism[J]. Nature, 1992, 359 (6397) : 710-712. doi: 10.1038/359710a0
[2]	Zhao D, Huo Q, Feng J, et al. Nonionic triblock and star diblock copolymer and oligomeric surfactant syntheses of highly ordered, hydrothermally stable, mesoporous silica structures[J]. J. Am. Chem. Soc., 1998, 120 (24) : 6024-6036. doi: 10.1021/ja974025i
[3]	Croissant J G, Fatieiev Y, Almalik A, et al. Mesoporous silica and organosilica nanoparticles: Physical chemistry, biosafety, delivery strategies, and biomedical applications[J]. Adv. Healthc. Mater., 2018, 7 (4) : 1700831.
[4]	Liang C, Li Z, Dai S. Mesoporous carbon materials: Synthesis and modification[J]. Angew. Chem. Int. Ed., 2008, 47 (20) : 3696-3717. doi: 10.1002/anie.200702046 pmid: 18350530
[5]	Ryoo R. Birth of a class of nanomaterial[J]. Nature, 2019, 575 (7781) : 40-41. doi: 10.1038/d41586-019-02835-7
[6]	Suib S L. A review of recent developments of mesoporous materials[J]. Chem. Rec., 2017, 17: 1169-1183. doi: 10.1002/tcr.v17.12
[7]	Wang R L, Habib E, Zhu X X. Synthesis of wrinkled mesoporous silica and its reinforcing effect for dental resin composites[J]. Dental Materials, 2017, 33 (10) : 1139-1148. doi: S0109-5641(17)30075-1 pmid: 28797746
[8]	Manzano M, Vallet-Regi M. Mesoporous silica nanoparticles for drug delivery[J]. Advanced Functional Material, 2019, 30 (2) : 1902634.
[9]	Lusi E, Ratna B, Takashi O, et al. Tunable synthesis of mesoporous silica particles with unique radially oriented pore structures from tetramethyl orthosilicate via oil-water emulsion process[J]. Langmuir, 2017, 33 (3) : 783-790. doi: 10.1021/acs.langmuir.6b04023 pmid: 28026955
[10]	Deng Y, Cai Y, Sun Z, et al. Multifunctional mesoporous composite microspheres with well-designed nanostructure: A highly integrated catalyst system[J]. J. Am. Chem. Soc., 2010, 132 (24) : 8466-8473. doi: 10.1021/ja1025744 pmid: 20507122
[11]	Wang H M, Liu X, Liu X, et al. Fluidisable mesoporous silica composites for thermochemical energy storage[J]. Energy, 2023, 275: 127255. doi: 10.1016/j.energy.2023.127255
[12]	Xu X, Song C, Andresen J M, et al. Preparation and characterization of novel CO₂ “molecular basket” adsorbents based on polymer-modified mesoporous molecular sieve MCM-41[J]. Environ. Sci. Technol., 2003, 37 (20) : 4667-4673.
[13]	Kohno Y, Haga E, Yoda K, et al. Adsorption behavior of natural anthocyanin dye on mesoporous silica[J]. J. Phy. Chem. Solids, 2014, 75: 48-51. doi: 10.1016/j.jpcs.2013.08.007
[14]	Manzano M, Aina V, Arenal R, et al. Studies on MCM-41 mesoporous silica for drug delivery: Effect of particle morphology and amine functionalization[J]. Chem. Eng. J., 2008, 137 (1) : 30-37. doi: 10.1016/j.cej.2007.07.078
[15]	Chu W C, Peng D R, Bastakoti B P, et al. Co-templating synthesis of bimodal mesoporous silica for potential drug carrier[J]. Chemistry Select, 2016, 1: 1339-1346.
[16]	Chen-Yang Y W, Chen Y T, Li C C, et al. Preparation of UV-filter encapsulated mesoporous silica with high sunscreen ability[J]. Materials Letters, 2011, 65: 1060-1062. doi: 10.1016/j.matlet.2010.12.034
[17]	Olejnik A, Goscianska J. Hybrid systems based on avobenzone-wrinkled mesoporous silica as ingredients of sunscreen formulations[J]. Micropor. Mesopo. Mat., 2024, 367: 112949. doi: 10.1016/j.micromeso.2023.112949
[18]	Arshad T, Shoaib Khan H M, Akhtar N, et al. Structural elucidation and development of azelaic acid loaded mesoporous silica nanoparticles infused gel: Revolutionizing nanodrug delivery for cosmetics and pharmaceuticals[J]. Heliyon, 2024, 10 (8) : 29460.
[19]	Moon D S, Lee J K. Formation of wrinkled silica mesostructures based on the phase behavior of pseudoternary systems[J]. Langmuir, 2014, 30 (51) : 15574-15580. doi: 10.1021/la504207k
[20]	富燕红, 凌峰, 王克奇. 优化防晒剂的SunSpheres^TM空心球体技术[J]. 日用化学品科学, 2000, 23 (4) : 43-45.

油脂		吸油值/（mL/100 g）
油脂		OSMS	150H	KSP-100	TAPIOCA
合成油脂类	辛酸/癸酸甘油三酯	247.4±5.3	152.5±5.3	45.5±3.7	37.7±2.4
	碳酸二辛酯	248.0±5.6	149.8±3.3	75.3±3.9	38.5±1.3
	二异硬脂醇苹果酸酯	232.5±2.7	135.8±5.0	48.2±1.9	32.5±1.6
	十三烷醇偏苯三酸酯	226.6±5.3	150.5±8.6	37.9±3.7	35.1±4.4
植物油脂类	霍霍巴籽油	259.0±4.0	160.7±4.2	46.2±4.0	42.4±3.4
植物油脂类	白池花籽油	246.2±4.0	142.5±1.6	38.8±2.7	33.0±1.1
烷烃类	角鲨烷	277.9±3.9	153.8±2.5	56.3±4.5	39.1±0.8
烷烃类	矿油	258.0±3.5	150.0±6.2	67.0±3.8	38.5±3.0
硅油类	环五聚二甲基硅氧烷	266.7±5.5	143.4±4.2	76.7±2.9	43.0±0.6
硅油类	聚二甲基硅氧烷	244.6±3.8	147.2±1.8	71.2±1.2	40.7±1.2

测试时间/h	相对皮脂吸附率/%
测试时间/h	0.3%	0.5%	1.0%	2.0%	3.0%
0.5	40.43±5.46^***	40.30±4.59^***	41.36±3.78^***	76.60±3.05^***	97.73±1.84^***
1.0	26.16±4.21^***	26.02±4.36^**	34.47±4.29^***	65.04±3.91^***	85.65±3.88^***
2.0	18.52±5.12^**	16.10±5.89^*	36.11±6.87^***	51.57±7.05^***	69.72±4.72^***
4.0	6.18±4.15 ^n.s.	12.44±4.04^*	23.54±5.81^**	32.07±6.51^*	44.63±7.57^***

Synthesis of open-pored mesoporous silica and its application in cosmetics

RichHTML

PDF (PC)

Like

Knowledge

Abstract

Cite this article

share this article

Figures/Tables 7

References 20

Related Articles 3

Metrics

Comments

Recommended 10

[1]	Meng Yu, Guorui Xu, Xiang Li, Yufei Zheng, Xuan Feng, Jinzhou Yang, Fenggang Liu. Experimental research of inorganic composite deep profile control and oil displacement agent for offshore high water cut oil fields [J]. China Surfactant Detergent & Cosmetics, 2024, 54(11): 1307-1312.
[2]	Niu Hongbo,Yan Yongli,Dou Longlong,Jiang Xuanxuan,Zhang Xiao,Zhang Peiliang. Advances in size control of micro and nano silica particles [J]. China Surfactant Detergent & Cosmetics, 2022, 52(7): 770-777.
[3]	GAO Yan-li,SUN Chen-ya,QI Li-yun,FANG Yun. Preparation of organo-montmorillonite modified with quaternary ammonium surfactant and its adsorption behavior for phenol [J]. China Surfactant Detergent & Cosmetics, 2016, 46(2): 61-65.