单分散聚甲基丙烯酸甲酯微球为模板制备大孔氧化铝材料

张勇¹, 孔庆岚², 刘芝平², 延姗姗², 于峰²

1.太原理工大学水利科学与工程学院,山西太原 030024;
2.太原理工大学化学化工学院,山西太原 030024

收稿日期:2018-03-16 发布日期:2019-03-18
通讯作者: 于峰,副教授,博士,电话:(0351)6018384,E-mail:yufeng@tyut.edu.cn。
作者简介:张勇(1980-),男,山西阳曲人,工程师,博士研究生,电话:(0351)6010250,E-mail:zy9506@163.com。
基金资助:
国家自然科学基金资助项目(21706176)

Preparation of macroporous aluminium oxide by using mono-dispersed PMMA microspheres as templates

ZHANG Yong¹, KONG Qing-lan², LIU Zhi-ping², YAN Shan-shan², YU Feng²

1.College of Water Resource Science and Engineering,Taiyuan University of Technology,Taiyuan,Shanxi 030024,China;
2.College of Chemistry and Chemical Engineering,Taiyuan University of Technology,Taiyuan,Shanxi 030024,China

Received:2018-03-16 Published:2019-03-18

摘要/Abstract

摘要： 以过硫酸铵为引发剂、十二烷基硫酸钠为乳化剂、甲基丙烯酸甲酯为单体,通过乳液聚合制备了聚甲基丙烯酸甲酯(PMMA)乳胶微球。研究显示,通过改变合成体系中乳化剂用量可对合成的PMMA微球的粒径进行有效调控,并得到了粒径分布在200~300 nm的PMMA微球;通过破乳沉降法加速PMMA微球的自组装,得到紧密堆积的PMMA微球胶体模板。将溶解在乙醇(经盐酸酸化)中的异丙醇铝溶液填充到组装好的PMMA胶体模板剂的空隙中,通过焙烧去除模板制得大孔氧化铝材料,在950 ℃焙烧3 h得到了规整大孔γ-Al₂O₃;扫描电镜和透射电镜结果表明所得材料孔道丰富,为三维有序大孔材料。

关键词: 聚甲基丙烯酸甲酯微球, 单分散, 胶体模板, 三维有序大孔材料

Abstract: Mono-dispersed polymethyl methacrylate (PMMA) latex microspheres were prepared by emulsion polymerization using ammonium persulfate as initiator,sodium dodecyl sulfate as emulsifier and methyl methacrylate as monomer.The results show that the particle size of the as-synthesized PMMA microspheres can be effectively controlled and adjusted by changing the content of emulsifier.The PMMA microspheres with diameter distribution of 200~300 nm were obtained.The self-assembly of PMMA microspheres was accelerated by demulsification sedimentation method so as to obtain a tightly packed PMMA microsphere colloidal template.The solution of aluminum isopropoxide dissolved in ethanol (acidified by hydrochloric acid) was filled into the interspaces of the PMMA colloidal template.The macroporous material of alumina was then obtained by roasting the template.γ-Al₂O₃ three-dimensionally ordered macroporous material (3DOM) was obtained by calcination at 950 ℃ for 3 h.The results of SEM and TEM show that the material is 3DOM which has many porous channels.

Key words: polymethyl methacrylate microsphere, mono-dispersed, colloidal template, three-dimensionally ordered macroporous material

中图分类号:

O631.2

张勇, 孔庆岚, 刘芝平, 延姗姗, 于峰. 单分散聚甲基丙烯酸甲酯微球为模板制备大孔氧化铝材料[J]. 日用化学工业, 2018, 48(6): 336-340.

ZHANG Yong, KONG Qing-lan, LIU Zhi-ping, YAN Shan-shan, YU Feng. Preparation of macroporous aluminium oxide by using mono-dispersed PMMA microspheres as templates[J]. China Surfactant Detergent & Cosmetics, 2018, 48(6): 336-340.

参考文献

[1] Kong Qinglan.Nano-zeolite and its self-assembly on the organic template for the preparation of macroporous zeolite [D].Taiyuan:Taiyuan University of Technology,2017.
[2] Kong Qinglan,Yan Shanshan,Cui Xingyu,et al.Synthesis of mono-dispersed polystyrene microspheres and application in preparation of three dimensional ordered macroporous (3DOM) materials [J].New Chemical Materialsm,2017,45(11),44-45.
[3] Bi Shenshen,Li Jing,Dong Dianquan.Preparation of polystrene microspheres and assembly and apply of tree-dimensional ordered colloidal crystal template [J].New Chemical Materials,2015,40(5),136-138.
[4] Zhou Qian,Dong Peng,Cheng Bingying.Three-dimensionally ordered self-assembly of SiO₂ colloidal particles [J].Chemistry,2004,67(4):290-294.
[5] Velev O D,Jede T A,Lobo R F, et al.Porous silica via colloidal crystallization [J].Nature,1997,389(6650):447-448.
[6] Li Shi,Zhao Dongfeng,Zheng Jingtang.Studies on preparation and characterization of 3DOM TiO₂ and TiO₂/SiO₂ materials with high photocatalytic ability [J].J.Porous.Mater.,2013,20(3):473-479.
[7] Deng Yonghui,Liu Chong,Yu Ting.Facile synthesis of hierarchically porous carbons from dual colloidal crystal/block copolymer template approach [J].Chem.Mater.,2007,19(13):3271-3277.
[8] Wang Xiaodong,Dong Peng,Yi Guiyun.Evaporation self-assembly method to fabricate high-quality polystyrene microsphere colloid crystal [J].Acta Physica Sinica,2006,55(4):2092-2098.
[9] Holgado M,GarcíaSantamaría F,Blanco A,et al.Electrophoretic depo-
sition to control artificial opal growth [J].Langmuir,1999,15:4701-4704.
[10] He Fang,Zhao Kun,Huang Zhen,et al.Synthesis of three-dimensionally ordered macroporous LaFeO₃ perovskites and their performance for chemical-looping reforming of methane [J] Chinese J.Catal.,2013,34(6):1242-1249.
[11] Srinivasan K.Crystal growth of α and γ glycine polymorphs and their polymorphic phase Transformations [J].Journal of Crystal Growth,2008,311(1):156-162.
[12] Zheng Jiajun,Yi Yuming,Wang Wenli,et al.Synthesis of bi-phases composite zeolites MFZ and its hierarchical effects in isopropylbenzene catalytic cracking [J].Micropor.Mesopor.Mater.,2013,171,44-52.
[13] Shen Yong,Wu Quanzhou Liao Jufang,et al.Synthesis and characterization of three-dimensionally ordered (3DOM) titania-silica mixed oxides [J].Journal of Inorganic Materials,2003,18(2):401-406.

单分散聚甲基丙烯酸甲酯微球为模板制备大孔氧化铝材料

Preparation of macroporous aluminium oxide by using mono-dispersed PMMA microspheres as templates

PDF (PC)

赞

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 1

Metrics

本文评价

推荐阅读 10