负载玫瑰香精多孔微球的制备及缓释性能研究

doi:10.13218/j.cnki.csdc.2015.01.009

摘要/Abstract

摘要： 以分散聚合合成的单分散聚苯乙烯微球作为种子微球,采用两步种子溶胀法制备多孔聚苯乙烯-二乙烯苯微球,并吸附玫瑰香精制备了香精多孔微球。利用马尔文激光粒度仪、比表面积孔径分布测定仪(BET)、热重分析仪(TGA)、扫描电镜(SEM)对种子微球和多孔微球的粒径、比表面积和孔结构、缓释性能、表观形貌进行了分析表征。结果表明:种球的粒径随着分散介质中无水乙醇体积分数的增大而增加;随着溶胀剂邻苯二甲酸二丁酯(DBP)用量的增加,多孔微球的平均粒径变大,分布变宽;随着交联单体二乙烯苯(DVB)用量增加,多孔微球平均粒径减小,分布变窄;以甲苯为致孔剂制备的多孔微球单分散性最好。当V(DBP)∶m(种球)=3∶1,V(DVB)∶V(苯乙烯)=4∶0时,制备的多孔微球的平均粒径约为4 μm。以此多孔微球负载玫瑰香精,可以减缓香精的释放速率,提高起始分解温度,实现对香精的缓释。

关键词: 玫瑰香精, 分散聚合, 种子溶胀, 多孔微球, 缓释

Abstract: Porous microspheres encapsulated with rose fragrance were prepared by adsorption of the fragrance on porous polystyrene-divinylbenzene (PSt-DVB) microspheres,which were obtained by two-step swell polymerization with the uniform polystyrene microspheres as seed particles via dispersion polymerization.The surface features of seed particles and porous microspheres were observed by scanning electron microscope (SEM);the particle size,the specific surface area and pore structure were analyzed and characterized by particle size analyzer and Brunauer,Emmett and Teller (BET) method;controlled-release performance was tested by thermal gravimetric analysis (TGA).The results showed that the particle size of the seed particles increases with the increasing of volume fraction of the ethanol.As dosage of the swelling agent,p-dibutyl phthalate (DBP) increases,particle size of the porous microspheres increases and its distribution becomes wider.As the dosage of cross-linking monomer DVB increases,average particle size of the porous microspheres reduces and its distribution becomes narrower.The best single size dispersion was obtained as the porous microspheres were generated with toluene.The porous PSt-DVB microspheres with the diameter of 4 μm were obtained when the ratio of V(DBP)∶m(seed particles) and V(DVB)∶V(St) is 3∶1 and 4∶0,respectively.As a result,the release rate of the fragrance can be slow down and initial decomposition temperature can be raised;and then the controlled release of the fragrance can be realized.

Key words: rose fragrance, dispersion polymerization, seed-swelling, porous microspheres, slow-release

中图分类号:

TQ655

苏忠毅, 裴广玲. 负载玫瑰香精多孔微球的制备及缓释性能研究[J]. 日用化学工业, 2015, 45(1): 36-40.

SU Zhong-yi, PEI Guang-ling. Preparation of porous microspheres encapsulated with rose fragrance and its slow-release performance[J]. China Surfactant Detergent & Cosmetics, 2015, 45(1): 36-40.

参考文献

[1] UNSAL E,CAMLI S T,SENEL S,et al.Chromatographic performance of monodisperse-macroporous particles produced by modified seeded polymerization [J].Applied Polymer Science,2004,92(1):607-618.
[2] SINGH A,YADAVR K,SRIVASTAVA A.Synthesis of resole-type phenolic beads from phenol and formaldehyde by suspension polymerization [J].Applied Polymer Science,2009,112(2):1005-1011.
[3] HONG J,HAN H,HONG C K,et al.A direct preparation of silica shell on polystyrene microspheres prepared by dispersion polymerization with polyvinylpyrrolidone [J].Polymer Science Part A:Polymer Chemistry,2008,46:2884-2890.
[4] OKUBO M,SHIOZAKI M.Production of micron-size monodisperse polymer particles by seeded polymerization utilizing dynamic swilling method with cooling process [J].Polymer International,1993,30(4):469-474.
[5] UGELSTAD J.Preparation and application of monodisperse polymer particles [J].Polymer Science Part A:Polymer Chemistry,1985,72(2):225-236.
[6] 马光辉,苏志国.高分子微球材料[M].北京:化学工业出版社,2005:11.
[7] VINU A,MORI T,ARIGA K.New families of mesoporous materials [J].Science and Technology of Advanced Materials,2006,7(8):753-771.
[8] 郑玮,王进美.芳香纺织品生产方法及应用现状[J].纺织科技进展,2008(2):17,39.
[9] 潘小会,王进美,吴铁城.艾叶提取物驱蚊微胶囊的制备[J].合成纤维,2012,41(1):27-30,51.
[10] 朱强,孙庆元,蒙敏,等.淀粉微球对玫瑰香精的吸附及缓释性能研究[J].日用化学工业,2008,38(4):238-241.
[11] HEINZE F,CLASEN M.Microspherules:US,5496565 [P].1996-03-05.
[12] 张晓宁,杨景辉,马新胜,等.种子溶胀法制备单分散交联苯乙烯微球[J].塑料工业,2009,37(3):37-39,42.
[13] 李璐,文秀芳,皮丕辉,等.种子溶胀聚合制备苯乙烯-二乙烯苯多孔交联微球[J].精细化工,2006,23(6):527-531.
[14] 李森,王宽,韦宝卿,等.新型TiO₂/聚合物复合粒子的制备及在化妆品中的应用[J].香料香精化妆品,2007(5):44-48.
[15] 朱琳.不同物性聚苯乙烯粒子的制备及其对生物学效应的影响[D].北京:北京化工大学,2013.
[16] MARK JE E.Polymer data handbook [M].Oxford:Oxford University Press,1999.
[17] MICHAEL R,PALPH H C.Polymer physics [M].励杭泉,译.北京:化学工业出版社,2007:109-112.